Bolas de Molienda / B2
B2 Bola de Molienda
C: 0.70–0.85%, Cr: 0.40–0.80%, Mn: 0.50–1.00% | 60–65 HRC
Iron ore, coal and clinker grinding circuits
Especificaciones Técnicas
Composición Química
C: 0.70–0.85%, Cr: 0.40–0.80%, Mn: 0.50–1.00%
Dureza
60–65 HRC
Aplicación
Iron ore, coal and clinker grinding circuits
Rango de Diámetros
Φ20 mm – Φ150 mm
Normas
GB/T 17445, ISO 3290, ASTM A532
Tratamiento Térmico
Quenching & Tempering
Tabla de Dimensiones
| Diámetro | Peso | Dureza | Tolerancia |
|---|---|---|---|
| 30 mm | 0.111 kg | Superficie > 58 HRC, Núcleo > 57 HRC | ±2 mm |
| 40 mm | 0.264 kg | Superficie > 58 HRC, Núcleo > 57 HRC | ±2 mm |
| 50 mm | 0.515 kg | Superficie > 58 HRC, Núcleo > 55 HRC | ±3 mm |
| 60 mm | 0.890 kg | Superficie > 58 HRC, Núcleo > 55 HRC | ±3 mm |
| 70 mm | 1.413 kg | Superficie > 58 HRC, Núcleo > 55 HRC | ±3 mm |
| 80 mm | 2.110 kg | Superficie > 58 HRC, Núcleo > 55 HRC | ±3 mm |
| 90 mm | 3.004 kg | Superficie > 58 HRC, Núcleo > 55 HRC | ±4 mm |
Otros Grados
60Mn
Composición Química: C: 0.55–0.65%, Mn: 0.70–1.00%
Dureza: 55–60 HRC
Cement and limestone grinding mills
65Mn
Composición Química: C: 0.65–0.75%, Mn: 0.90–1.20%
Dureza: 58–63 HRC
Metal ore and hard rock grinding
B3
Composición Química: C: 0.70–0.90%, Cr: 0.80–1.20%, Mo: 0.20–0.50%
Dureza: 62–66 HRC
High-impact and abrasive grinding environments
HIGH-CR
Composición Química: C: 1.00–1.30%, Cr: 10–12%
Dureza: 60–68 HRC
Gold, copper and highly abrasive ore grinding